146 research outputs found
Effect of KOH molarity on structure, morphology, and optical properties of flower-like CuO nanostructures synthesized by ultrasonic-assisted precipitation method
No full textLink to publisher's homepage at http://ijneam.unimap.edu.myThis paper reports the effect of KOH molarity variation on structure, morphology, and optical properties of CuO nanostructures synthesized by ultrasonic-assisted precipitation method. The results of the XRD analysis showed that the CuO samples had a monoclinic structure with lattice constants which decreased with increasing KOH molarity in the sonochemical precursors. The average crystallite size (ACS) of the CuO samples depend on the KOH molarity, which tends to decrease (in the range 16-23 nm) with increasing KOH molarity. Small ACS indicates that the CuO samples tend to have a nanocrystal structure. The morphology of the CuO samples is also influenced by the KOH molarity, which the flower-shaped CuO nanostructure was found for low molarity (0.25 M) of KOH in the sonochemical precursor. The optical characteristics of CuO samples strongly absorb the wide spectrum of electromagnetic waves below 650 nm. The bandgap energy of the CuO samples has a fairly large value and fluctuates in the range of 1.74 - 1.82 eV which varies with the molarity of KOH in the precursor solutions
The effect of sintering temperature on structure and electrical properties of CaTiO3 synthesized from hen’s eggshell via hydrothermal process
Get PDFLink to publisher's homepage at http://ijneam.unimap.edu.myThis article reports the effect of the sintering temperature on structural and electrical properties of CaTiO3 synthesized via a hydrothermal route from hen’s eggshell waste as a calcium source. The eggshell-derived powder was reacted with a commercial TiO2 powder in the hydrothermal reactor then sintered in a furnace with varied temperatures. The result of X-ray diffraction analysis shows that the crystal phase of the CaTiO3 samples depended on the sintering temperature. As the sintering temperature increased, the crystal phase of starting materials and secondary products decreasing, as a result, the crystal phase of CaTiO3 sample to become purer. The SEM image shows that CaTiO3 grains become finer and more uniform as the sintering temperature increases. The result of I-V characterization confirmed that sintering temperature greatly affected the electrical properties of CaTiO3. The electrical parameter of CaTiO3 samples was affected by sintering temperature, where the resistance of CaTiO3 increased with the increasing sintering temperature. Whereas the resistivity of CaTiO3 samples decreases with increasing sintering temperature, vice versa with the electrical conductivity
Penilaian Sejawat Jurnal Ilmiah Harry Ramza; Analysis of TE (Transverse Electric) Modes of Symmetric Slab Waveguide
Get PDFLembar Penilaian Sejawat ditanda tangani oleh; Reviewer 1 : Dr. Akhiruddin, Maddu, M.Si. (Fisika, FMIPA - IPB, Bogor) Reviewer 2 : Sugianto S.Si, M.Si (Pendidikan Fisika, FKIP - UHAMKA, Jakarta
Penilaian Sejawat Jurnal Ilmiah Harry Ramza; "The Critical Observation ...."
Get PDFLembar Penilaian Sejawat ditanda tangani oleh;
Reviewer 1 : Dr. Akhiruddin, Maddu, M.Si. (Fisika, FMIPA - IPB, Bogor)
Reviewer 2 : Sugianto S.Si, M.Si (Pendidikan Fisika, FKIP - UHAMKA, Jakarta
Efek Fotovoltaik Pada Persambungan CdS/P3HT-Kitosan.
Get PDFA CdS/Polymer junction has been fabricated and it’s photovoltaic effect has been studied. The polymer is a blend of poly-3hexyltiophene (P3HT), chitosan and polyethileneglicol (PEG). Boron in situ doping of CdS using Chemical Bath Deposition (CBD) was investigated. The effect of B-doping and annealing on optical properties as well as on electrical and morphology of CdS film were studied. The structure and morphology of the film were detected by XRay Diffraction (XRD) and Scanning Electron Microscopy (SEM). The polymer film was sandwiched between the CdS semiconductor and an ITO glass to form an ITO/CdS/Polymer/ITO photovoltaic cell. Time constant (τ) and open circuit voltage (Voc) were investigated by using voltage censor. The bandgap of films were determined using absorbance edge method. The results of annealing optical bandgap of undoped CdS shifted from 2,49 eV down to 2,39 eV. Phase transition of CdS due to annealing temperature and induced lattice damage due to doping. The room temperature conductivity of polymer is 3,8 – 6,6 x 10-7 S/cm as function of frequency between 100 – 5000 Hz. The Voc of the fabricated cells ranges between 107 – 286 mV and time constant ranges between 2,5 to 43,75 s.Energi matahari merupakan energi yang terbesar di permukaan bumi. Energi ini dapat dimanfaatkan secara langsung maupun secara tidak langsung. Energi matahari dapat dikonversi menjadi energi listrik dalam mekanisme fotovoltaik. Piranti pengkonversi energi matahari menjadi energi listrik dapat dibuat dengan menyambungkan antara semikonduktor tipe-p dan semikonduktor tipe-n. Cadmium sulfida merupakan salah satu jenis semikonduktor tipe-n dimana mempunyai dua struktur kristal yaitu kubik dan heksagonal. CdS memiliki gap energi sebesar 2,3-2,5 eV. CdS fase kubik merupakan fase metastabil dimana dapat berubah menjadi fase heksagonal jika diannealing pada suhu di atas 300o Poly3-heksiltiophene adalah semikonduktor tipe-p yang merupakan turunan dari polimer tiophene. Polimer ini memiliki mobilitas hole yang tinggi dan stabil di lingkungan udara maupun dalam air. Jika polimer ini digabungkan dengan polimer jenis lain, maka pembawa muatan pada polimer ini akan bertambah. Dengan adanya pembawa muatan yang banyak ini maka akan meningkatkan kinerja persambungan yang akan dibuat. C. Metode pembuatan CdS dapat dilakukan dengan sangat mudah. Selain itu bahan yang digunakan pula sangat mudah didapatkan. Cadmium sulfida dibuat dengan metode Chemical Bath Deposistion (CBD), menggunakan CdCl2 sebagai sumber ion cadmium, CS(NH2)2 sebagai sumber ion sulfur, NH4OH sebagai agen pengkompleks dan mengatur kecepatan reaksi serta TEA untuk mempertahankan larutan agar tidak cepat mengendap. Dua bahan yang pertama diaduk dengan kelajuan 300 rpm selama 30 menit pada suhu 30oC. Selanjutnya ditambahkan NH4OH dan TEA dan diaduk dengan kelajuan yang sama selama 90 menit pada suhu 70oC. Pemberian doping Boron dilakukan dengan penambahan asam borat (H3BO3) dengan jumlah masing-masing 4% wt, 6%wt dan 8%wt. Pemberian doping Boron ini dimaksudkan untuk mengubah gap energi CdS yang dihasilkan. Selanjutnya film tipis yang dihasilkan diannealing pada suhu 200oC, 300oC dan 400oC selama 1 jam dengan kenaikan suhu 1oC/menit. Film-film ini selanjutnya dikarakterisasi UV-Vis, XRD dan SEM masing-masing untuk mengetahui pita serapan, struktur kristal dan morfologi film yang dihasilkan. Di atas film yang dihasilkan selanjutnya ditetesi dengan polimer campuran antara P3HT dengan kitosan dengan menggunakan metode drop casting agar diperoleh ketebalan polimer yang sama pada permukaan film CdS. Persambungan ini selanjutnya diukur respon dinamik dan kestabilan tegangannya dengan menghubungkannya dengan sensor tegangan. Pengukuran ini sangat penting dilakukan untuk mengetahui seberapa besar tegangan rangkaian terbuka (Voc) yangt dihasilkan pada persambungan ini
Application of phycocyanin from microalgae Spirulina platensis as light harvesting in anatase TiO2 nanoparticle solar cell.
No full textThe dye sensitized solar cell (DSSC) has been assemblied used hybrid titanium oxide (TiO2) film/phycocyanin. The TiO2 film was synthesized by sol gel method with titanium chlorida (TiCl4) as precursor by hydrolysis used sulfuric acid (H2SO4). Furthermore, it calcinated for 2,5 hours in variation of annealing temperature (400oC, 600oC, 800oC, dan 1000oC). In XRD patterns exhibited which annealing temperature at 400oC to 800oC were anatase phase all. When annealed at temperature 1000oC, it caused phase transformation from anatase to rutile. The crystals size according to XRD patterns were 13,75 nm, 20,79 nm, 25,25 nm, 48,88 nm and particle size from SEM images were 43,06 nm, 44,91 nm dan 64,99 nm, 80,40 nm, respectively. The crystals and particle size increased with annealing temperature. The film thickness influenced material absorption. The optical measurement of TiO2 film and TiO2/phycocyanin hybrid film used UV-Vis spectrophotometer. Additional phycocyanin caused peak width of absorbed region from ultraviolet to visible region. The band gap energy of TiO2 can be calculated using the cut off wavelength obtained from the absorbance spectrum of a nanoparticles TiO2 films. Based on intersection between linear and energy (hv) axis. In this study just limited for anatase phase. It was caused anatase band gap is wider than rutile phase. That’s meaningful for solar cell application such as dye sensitized solar cell (DSSC). The absorption coefficient average at difference annealing temperature such as at 400oC, 600oC, 800oC were 8,1600x102, 1,7535x103 and 4,0154x102, where α < 104 include to direct transition. Band gap energy 400oC, 600oC, 800oC were 3,79 eV, 3,59 eV, and 3,35 eV, respectively. Based on this result, exhibition that band gap energy of TiO2 semiconductor film decreased with increasing annealing temperature. Spirulina platensis was cultivated in technical modification (Hastuti) with aeration under light intensity about 3000 lux. The cell density (stationer phase) for eighth day which OD value was more than 0,5. It means, the culture can be harvested. In 80 liters Spirulina platensis culture have been produced biomass dry about 10,46 gram and extracted phycocyanin in dry powders was 5,50 gram. The phycocyanin absorption spectrum at the wavelength of 619,36 nm (visible region) which had relaxation energy was 2,945 eV. The emission peak at the wavelength of 708,55 nm with relaxation energy about 2,793 eV. The Stokes shift based on difference energy absorption and emission calculated about 0,152 eV. Both of this showed phycocyanin can absorbed and radiated the sun light which received. This choice characteristic pigment was a good one related to sensitizer in solar cell application. Integration between light harvesting protein and TiO2 semiconductor surface had important role in improving of output as solar cell materials. The presence of carboxylate group (-COOH) made pigment be more efficient was due to anchored to the surface of TiO2 ampoter. The phycocyanin pigment had carboxylate group which reacted with TiO2 surface formed ester. The carboxylate group increased of dye electronics couple from excited state (p anti bonding orbital) to semiconductor acceptor state (TiO2 conduction band). The samples which made based on annealing temperature variation formed be solar cell respectively. Furthermore, cells be assembled for current-voltage (I-V) measurement under direct sun light with intensity about 120 Watt/m2. The measurement result consists of Isc (short circuit) if voltage was zero, Voc (open circuit voltage) where external load was highest, Vmax when voltage provided maximum power and Imax when current produced maximum power. The fill factor (FF) was ratio between Vmax Imax and Voc Isc. The efficiency be calculated by comparison between power of solar cell result and light power which attracted. The cell potentiality converted sunlight into electrical energy with highest efficiency resulted for cell at 800oC calcinated temperature was 1,04%. The annealing temperature at 400oC lesser than cell calcinated at 600oC was 0,29%. From the result, Voc and Isc increased with increasing of TiO2 annealing temperature. Moreover, increasing of annealing temperature increased to the efficiency result
Prototype Material Penyerap Gelombang Radar dari Komposit Polimer Chitosan-Polivinil Alkohol
No full textTeknologi militer dalam menghadapi peperangan telah digunakan sejak abad ke-15. Penggunaan alat pendeteksi mutakhir seperti radar merupakan pilihan cerdas sebagai penghindaran diri dari serangan lawan, namun seiring dengan itu berkembang pula teknologi anti radar atau teknologi siluman (stealth). Pengembangan material penyerap gelombang elektromagnetik sebenarnya telah dimulai sejak tahun 1930, namun paten yang muncul baru pada tahun 1971 dan masih tergolong kepada material anorganik. Kecenderungan material penyerap gelombang radar baru sudah mulai mengarah juga kepada material organik. Chitosan merupakan salah satu material organik yang berpotensi untuk dikembangkan sebagai material penyerap gelombang radar. Sifat polikationik yang dimiliki, cenderung menggolongkan chitosan sebagai bahan dielektrik. Bahan dengan sifat dielektrik yang tinggi akan mampu menyimpan gelombang yang terserap dalam jumlah besar. Penelitian ini bertujuan untuk mengembangkan dan menganalisis karakteristik film penyerap gelombang radar dari komposit polimer chitosan-polivinil alkohol. Tahapan penelitian meliputi formulasi material untuk pembuatan film prototype penyerap gelombang radar, pembuatan material film, karakterisasi kualitas film, preparasi prototype penyerap gelombang radar, karakterisasi prototype penyerap gelombang radar. Formula material yang digunakan berupa campuran chitosan dan PVA dengan perbandingan chitosan : PVA (1 : 1). Konsentrasi larutan yang dicobakan terdiri atas campuran chitosan 1%; 1,5%; 2% dengan PVA 5%. Preparasi prototype dilakukan dengan perluasan paparan permukaan film menjadi ukuran 30 x 30 cm, yang bertujuan untuk meningkatkan daya penyerapan gelombang radar. Karakterisasi kualitas prototype penyerap gelombang radar dilakukan dengan pengujian reflection loss. Bentuk film yang telah dibuat menyerupai lembaran plastik tipis dan transparan dengan warna sedikit kekuningan. Film ini memiliki kekuatan tarik dari 106,33 ± 2,82 – 143 ± 2,59 kPa. Analisis SEM memperlihatkan struktur homogen yang ditandai dengan interaksi yang baik antara chitosan dengan PVA. Besar daya serap gelombang elektromagnetik (radar) oleh prototype film material ditunjukkan dengan makin besarnya nilai reflection loss. Nilai optimum didapatkan pada film prototype dengan material konsentrasi chitosan 1% yaitu berkisar pada -28,3127-38,8229 dB
Sintesis dan Sifat Mekanik Biokomposit Serat Heliconia-poliester
Get PDFIn this study, polyester-fiber heliconia biocomposites has been created and tested on its mechanical properties. Biocomposites was manufactured begins by separating the fibers. it consists of three stages, namely chlorization, alkaline leaching and extraction. After that, the manufacture of composites made with Hand Lay-up techniques. Three samples with variations in fiber content, ie without the addition of fiber, 0.54 g and 2.08 g fiber. Characterization of samples includes tensile test, hardness, and impact. The test results known that the tensile strength and hardness increased with increasing the amount of fiber heliconia. Impact test shows sample values optimum working temperature is 10°
Rancang bangun data logger berbasis sensor Dht22 untuk mengukur suhu dan kelembaban habitat satwa herpetofauna Secara real-time
No full textPada penelitian ini dilakukan perancangan data logger suhu dan kelembaban berbasis sensor DHT22 untuk pemantauan habitat satwa herpetofauna. Satwa herpetofauna sangat sensitif dengan perubahan suhu dan kelembaban habitatnya. Data dari sensor diteruskan melewati rangkaian buffer menuju mikrokontroler dan berakhir pada Data logger yang dibangun dari 3 komponen utama yaitu RTC peripheral (pewaktu), EMS SDcard (perekam), dan SDcard (media penyimpanan). Kemampuan minimal selang pengukuran alat adalah 5 detik setiap data. Hasil pengukuran dianalisis dengan metode ploting curve pada program Microsoft Excel 2007. Secara umum sebaran data menunjukan nilai suhu yang berbanding terbalik dengan kelembaban pada pengukuran di dalam lubang, dalam ruangan, dan luar ruangan. Komparasi alat ukur mendekati nilai komparator (termometer raksa) dibandingkan dengan alat Thermometer-Hygrometer TFA. Nilai ketepatan alat terhadap komparator sebesar 98%
Karakterisasi Optik dan Listrik Kalsium Titanat (CaTiO3) Hasil Sintesis Hidrotermal dan Annealing
No full textDalam penelitian ini dilakukan pembuatan material kalsium titanat (CaTiO3) melalui metode hidrotermal dan annealing. Pembuatan material CaTiO3 dengan menggunakan prekursor kalsium oksida (CaO) dari cangkang telur itik dan bubuk material TiO2. Perlakuan diawali dengan pembuatan kalsium oksida (CaO) yang diperoleh melalui transformasi kalsium karbonat (CaCO3) hasil kalsinasi. Untuk proses pembuatan CaTiO3 dengan melarutkan bubuk CaO dan bubuk TiO2 ke dalam larutan amoniak (NH4OH) menggunakan metode hidrotermal (suhu 2000C), kemudian bubuk CaTiO3 dipelet dan annealing pada tiga variasi suhu yaitu 7000C, 8000C dan 9000C. Ketiga sampel tersebut di karakterisasi dan dilakukan pengujian secara fisik. Pola XRD menunjukkan bahwa sampel CaTiO3 terbentuk optimal pada annealing suhu 9000C dengan ukuran kristal sebesar 38,36 nm. Sedangkan dari uji SEM dapat ditentukan ukuran butir kristal dari ketiga sampel CaTiO3 secara berturut-turut : 0,23 μm, 0,22 μm dan 0,25 μm. Pada karakterisasi optik, serapan yang paling tinggi terdapat di daerah ultra violet (UV) yaitu pada panjang gelombang 360-380 nm, sebaliknya merefleksikan di daerah visible dan infrared. Dari uji optik juga dapat ditentukan band gap dari suatu sampel. Nilai band gap yang diperoleh dari sampel CaTiO3 yang diannealing 7000C, 8000C dan 9000C secara berturut-turut yaitu 3,43 eV; 3,36 eV dan 3,34 eV. Dengan adanya kenaikan suhu pada sampel maka band gap yang diperoleh semakin kecil. Dari karakteristik listrik dapat disimpulkan bahwa pada sampel annealing suhu 7000C bersifat nonohmik, sedangkan pada sampel annealing suhu 8000C dan 9000C bersifat ohmik dan merupakan bahan semikonduktor. Hal ini ditunjukkan oleh nilai resistivitas dan konduktivitasnya yang masih berada pada range semikonduktor
- …