ИССЛЕДОВАНИЕ СВОЙСТВ ЭЛЕКТРОЭРОЗИОННЫХ ПОРОШКОВ И ТВЕРДОГО СПЛАВА, ПОЛУЧЕННОГО ИЗ НИХ ИЗОСТАТИЧЕСКИМ ПРЕССОВАНИЕМ И СПЕКАНИЕМ
Get PDFResults of the investigation into the properties of the hard alloy fabricated by isostatic pressing and sintering of powders prepared by EDM dispersion of tungsten-containing waste of the T15K6 alloy in distilled water and burning kerosene. An original installation developed and patented by the authors was used for EDM dispersion of conductive materials. Isostatic pressing of the powder was performed using an EPSI press (Belgium) at a pressure of 300 MPa and sintering was performed in a Nabertherm high-temperature furnace (Germany) in vacuum at 1500 °C for 2 h. The content of main elements (W, Ti, Co) both in powder and in the hard alloy fabricated from it was established using the electron probe microanalysis. Microhardness of powder and alloy is investigated and it is shown that powder prepared by EDM dispersion in kerosene and alloy made of it have increased HV compared with the samples fabricated using water as the working liquid.Представлены результаты исследования свойств твердого сплава, изготовленного изостатическим прессованием и спеканием порошков, полученных электроэрозионным диспергированием (ЭЭД) вольфрамсодержащих отходов сплавов Т15К6 в дистиллированной воде и керосине осветительном. Для ЭЭД токопроводящих материалов использована оригинальная установка, разработанная и запатентованная авторами. Изостатическое прессование порошка осуществлялось на прессе «EPSI» (Бельгия) при давлении 300 МПа, а спекание – в высокотемпературной печи «Nabertherm» (Германия) в вакууме при температуре 1500 °С в течение 2 ч. Рентгеноспектральным микроанализом установлено содержание основных элементов (W, Ti и Со) как в порошке, так и в полученном из него твердом сплаве. Исследована их микротвердость и показано, что порошок, полученный ЭЭД в керосине, и сплав из него имеют повышенную величину HV по сравнению с образцами, изготовленными с использованием в качестве рабочей жидкости воды
ИССЛЕДОВАНИЕ МЕХАНИЗМА ОБРАЗОВАНИЯ И СТРОЕНИЯ ВЫСОКОПОРИСТОГО ГУБЧАТОГО СЕРЕБРА
Get PDFThe methods of production and the results of investigation of high-porous spongy silver and morphology of its formation are presented. The product is shown to represent nanostructure consisting of silver particles of 100–200 nm in size, accreted with one another into conglomerates of branched forms. Examples of possible application of nanostructural high-porous spongy silver are given.Представлены методы получения и результаты исследования высокопористого губчатого серебра и морфологии его образования. Показано, что этот продукт представляет собой наноструктуру, состоящую из частиц серебра размером 100–200 нм, сросшихся между собой в конгломераты разветвленной формы. Даны примеры возможного использования наноструктурного высокопористого губчатого серебра
МОНИТОРИНГ ПОКАЗАТЕЛЕЙ РАБОТЫ АЛЮМИНИЕВЫХ ЭЛЕКТРОЛИЗЕРОВ С АНОДОМ СОДЕРБЕРГА
Get PDFAn analysis of the main technical-and-economic performance measures of one of aluminum works: OK «RUSAL» for a long run has been carried out. Technological advancement allowed raising considerably the efficiency of the electrolysis schematic with Soderberg anode. The prospects for the method development are shown in passing to a «colloidal» anode and the updated electrolysis bath design.Проведен анализ основных технико-экономических показателей работы одного из алюминиевых заводов ОК «РУСАЛ» за длительный период времени. Совершенствование технологии позволило значительно повысить эффективность схемы электролиза с анодом Содерберга. Показаны перспективы развития метода при переходе на «коллоидный» анод и модернизированную конструкцию электролизера
ОБЪЕМНЫЕ МЕТАЛЛИЧЕСКИЕ СТЕКЛА: ПОЛУЧЕНИЕ, СТРУКТУРА, СТРУКТУРНЫЕ ИЗМЕНЕНИЯ ПРИ НАГРЕВЕ
Get PDFBulk metallic glasses (BMGs) of Pd–Cu–Si and Pd–Ni–P system were formed from the melt in 1970s–1980s. However, in view of the extremely high cost of the main component (palladium), they were out of special interest for scientists and engineers for a long time. Relatively recently, BMGs in a form of macroscopic-size ingots here fabricated in alloys based on industrial metals (iron, copper, magnesium, and titanium), which opened wide possibilities for their application. BMGs possess high strength, hardness, wear resistance, elastic deformation, and corrosion resistance. In this study, a review of publications is presented and main scientific achievements in this field are described. It is noted that main scientific problems, which are not solved completely, are the description of the BMG structure as well as vitrification and plastic deformation, while the technical problem, which attracts attention of scientists in many countries, is an increase in plasticity and impact fracture toughness of these materials.Объемные металлические стекла (ОМС) систем Pd–Cu–Si и Pd–Ni–P были получены из расплава в 70–80-х годах прошлого века. Однако ввиду исключительной дороговизны основного компонента (палладия) они долгое время не представляли особого интереса для ученых и инженеров. Относительно недавно ОМС в виде слитков макроскопического размера были получены в сплавах на основе промышленных металлов (железа, меди, магния и титана), что открыло широкие возможности для их применения. ОМС обладают высокими показателями прочности, твердости, износостойкости, упругой деформации и сопротивления коррозии. В настоящей работе приведен обзор литературных источников и описаны основные научные достижения в данной области. Отмечено что главными, не до конца решенными научными проблемами являются описания структуры ОМС, а также процессов стеклования и пластической деформации, а технической задачей, приковывающей внимание ученых разных стран, – повышение пластичности и ударной вязкости данных материалов
ОСТАТОЧНЫЕ НАПРЯЖЕНИЯ В МЕДНЫХ И ЛАТУННЫХ ТРУБАХ ПОСЛЕ ВОЛОЧЕНИЯ
Get PDFThere was conducted simulation of process of final fixed plug drawing relating to tube from brass L96 with dimensions 8,0×0,2 mm. There were calculated residual stresses distribution on pipes walls with the aid of procedure that used method of «dissection of solids», taking into account condition of «conformity». Insignificance discrepancies of calculations and results of stimulation testified that offered procedure is adequately described process of residual stresses occurrence in tubes walls, and could be applied for the assessment of its level.Проведено моделирование процесса финишного короткооправочного волочения труб из латуни Л96 размером 8,0×0,2 мм. Рассчитаны распределения осевых остаточных напряжений по стенкам труб с помощью методики, использующей метод «расчленения тел» с учетом условия «совместности». Незначительные расхождения расчетов и результатов моделирования свидетельствуют о том, что предлагаемая методика адекватно описывает процесс возникновения в стенках труб остаточных напряжений и может применяться для оценки их уровня
КВАНТОВО-ХИМИЧЕСКОЕ ИССЛЕДОВАНИЕ ЭФФЕКТОВ ГИДРАТАЦИИ ДИЦИАНОАУРАТОВ В ЩЕЛОЧНЫХ СРЕДАХ
Get PDFUsing the DFT (B3LYP/LANL2DZ) quantum-chemical method, the dynamics of equilibrium change in chemical exchange in interacting dicyanoaurate with potassium hydroxide resulting in bimolecular hydroxy cyanoaurate complex with potassium cyanide has been studied. The study has been carried out for gas-phase and polyhydrated states with varied number (n) of water molecules in near-sphere environment. The equilibrium is fully shifted towards dicyanoaurate in gas-phase and poly-hydrated states (n ≤ 3). The subsequent increase of water molecules (n > 3) within the solvate environment of the bimolecular system results in the equilibrium shift towards hydroxy cyanoaurate formation.В рамках квантово-химического метода DFT(B3LYP/LANL2DZ) изучена динамика изменения равновесия в реакции обмена при взаимодействии дицианоаурата с гидроксидом калия, приводящей к бимолекулярному комплексу гидроксициано-аурата с цианидом калия. Исследование проведено для газофазного и полигидратированного состояний с варьируемым (n) количеством молекул воды в ближнесферном окружении. В газофазном и гидратированном (n ≤ 3) состояниях равновесие полностью сдвинуто в сторону дицианоаурата. Дальнейшее увеличение молекул воды (n > 3) в сольватном окружении бимолекулярной системы приводит к сдвигу равновесия в сторону образования гидроксицианоаурата
УПРОЧНЕНИЕ ТВЕРДОСПЛАВНОГО ЛЕЗВИЙНОГО ИНСТРУМЕНТА, ИСПОЛЬЗУЕМОГО ДЛЯ РЕЗАНИЯ ТРУДНООБРАБАТЫВАЕМЫХ ТИТАНОВЫХ СПЛАВОВ И ХРОМОНИКЕЛЕВЫХ СТАЛЕЙ, МНОГОСЛОЙНЫМИ НАНОСТРУКТУРНЫМИ ПОКРЫТИЯМИ
Get PDFComplex investigations into physicomechanical properties and adhesion strength in the «coating–carbide cutting insert» system of monolayered (Ti–Al–N) and multilayered (Ti–Al–N/Cr–N, Ti–Al–N/Zr–N/Cr–N) are performed. The advantage of using the latter; which is associated with the passage from the adhesion mechanism of coating destruction to the cohesion mechanism; with an increase in parameters H3/E2 and H/E that characterize the material resistance to plastic and elastic deformation, respectively; is shown. The introduction of chromium into the composition of Ti–Al–N coatings provides a decrease in friction coefficient (from 0,52 to 0,45) and a decrease in probability of adhesion interaction with the treated material. Comparative operational tests of carbide cutting insets (CCI) with coatings under study in the course of continuous cutting steel 12H18N10Т showed that largest wear resistance of Ti–Al–N/Zr–N/Cr–N coatings. Wear tests of CCIs made of VK6NST and TT10K8B alloys with Ti–Al–N/Zr–N/Cr–N coatings in the course of longitudinal turning steel 12H18N10Т and VT20 alloy evidence an increase in their resistance up to a factor of 3,0–3,5 both at low and high cutting rates. These coatings provide an increase in resistance of cutting tool and in milling operations of VT20 titanium alloy at cutting velocity up to 40 m/min
МОДЕЛИРОВАНИЕ ПРОЦЕССА ГЛУБОКОЙ ВЫТЯЖКИ ТРУБЧАТЫХ ПЕРЕХОДНИКОВ ИЗ СЛОИСТЫХ ТИТАНОАЛЮМИНИЕВЫХ ПЛАСТИН
Get PDFThere was described technological process of titanium-aluminium tubular coupling pieces from explosive welded stock material with the use of pressing operation. There was demonstrated possibility of stimulation with the aid of software package SIMULIA/Abaqus of the staged of deformation in deep drawing of layered titanium-aluminium composites, allowing to define permissible range of variation of the bending radii of punch and the leading edge of the die.Описан технологический процесс получения трубчатых титаноалюминиевых переходников из сваренных взрывом заготовок с использованием операций листовой штамповки. Показана возможность моделирования с помощью программного комплекса SIMULIA/Abaqus стадий деформирования при глубокой вытяжке слоистых титаноалюминиевых композитов, позволяющего определять допустимые диапазоны варьирования радиусов закругления пуансона и входной кромки матрицы
ОСОБЕННОСТИ ЭЛЕКТРООСАЖДЕНИЯ КОМПОЗИЦИОННЫХ ПОКРЫТИЙ «НИКЕЛЬ–НАНОПОРОШОК ДИБОРИДА ХРОМА»
Get PDFThe conditions for obtaining composite electrochemical coatings (CEC) have been investigated on the basis of nickel with the use of CrB2 nanopowder as a hardening phase in standard nickel-plating electrolyte. It is established that the maximum saturation of the nickel matrix in using chromium nanoboride takes place when its concentration in the electrolyte is 5–10 kg/m3 that is 8–12 times lower than in using micropowders. CEС microhardness of Ni–CrB2(nano) composition with the content of 0,59–0,65 % hardening phase is 1,16–1,19 times higher than that of Ni–CrB2(micro) coatings containing 2,47–2,86 % boride and 1,64–1,86 times higher than that of the nickel matrix. The optimum conditions of CEC deposition are cathodic current density of 1,0 kA/m2, nanoboride concentration of 5–10 kg/m3 in the electrolyte, pH 5,0–5,5, and temperature of 323 K.Исследованы условия получения композиционного электрохимического покрытия (КЭП) на основе никеля с использованием в качестве упрочняющей фазы нанопорошка CrB2 в стандартном электролите никелирования. Установлено, что максимальное насыщение никелевой матрицы при использовании наноборида хрома происходит при его концентрации в электролите 5–10 кг/м3, что в 8–12 раз ниже, чем при добавке микропорошков CrB2. Микротвердость КЭП состава Ni–CrB2(нано) при содержании в них упрочняющей фазы 0,59–0,65 % в 1,16–1,19 раз выше, чем у покрытий Ni–CrB2(микро), содержащих 2,47–2,86 % борида, и в 1,64–1,86 раз выше, чем у никелевой матрицы. Оптимальными условиями осаждения КЭП являются: катодная плотность тока 1,0 кА/м2, концентрация наноборида в электролите 5–10 кг/м3, рН = 5,0÷5,5 и температура 323 К
МОДЕЛИРОВАНИЕ ТРУБОВОЛОЧИЛЬНОГО ИНСТРУМЕНТА ПРИ ВОЛОЧЕНИИ МНОГОГРАННЫХ ТРУБ ИЗ ЦВЕТНЫХ МЕТАЛЛОВ НА НЕПОДВИЖНОЙ ОПРАВКЕ
Get PDFA method of mathematical simulation of tube-drawing tool for draw of many-sided tubes made of non-ferrous metals and alloys with the use of the vector-matrix tools, which can be applied for analytical description of the volume deformation region, is given. Reducing dies with various geometry of the squeezing zone are considered. As a result of the simulation of the deformation region arising in the course of producing section-shaped many-sided tubes by the mandrel drawing method with the use of all types of considered reducing dies, it is found that the best result with the least spherical radiuses is reached with reducing dies with the pyramidal input into the squeezing zone.Представлен способ математического моделирования трубоволочильного инструмента для волочения многогранных труб из цветных металлов и сплавов с использованием векторно-матричного аппарата, который может быть применен для аналитического описания объемного очага деформации. Рассмотрены волоки с различной геометрией обжимной зоны. В результате моделирования очага деформации, возникающего в процессе получения профильных многогранных труб методом оправочного волочения с использованием всех видов рассмотренных волок, установлено, что наилучший результат с наименьшими радиусами скругления достигается у волок с пирамидальным входом в обжимную зону