ПОЛУЧЕНИЕ АКТИВНОГО ГИДРОКСИДА АЛЮМИНИЯ И ЕГО ИСПОЛЬЗОВАНИЕ ДЛЯ ПРОИЗВОДСТВА МЕЛКОДИСПЕРСНОГО ГЛИНОЗЕМА
Get PDFActive aluminum hydroxide production from alkaline aluminate solution of the Bayer process by means of aluminum salt has been investigated. For this purpose the capacity of non-uniform growth of crystals at low temperatures and without mixing is used. Deposit of high specific surface, which is easily dissolved in acids and alkalis, is formed as consequence. Activation energy of produced active aluminum hydroxide being equal to 155.4 kJ/mole has been determined experimentally, thus indicating the kinetic mode of the process despite no mixing. The possibility of the produced active aluminum hydroxide application as a inoculating crystal for production of well-crystallized small-sized aluminum hydroxide powder, which can be used for production of aluminum oxide of non-metallurgical application, is shown.Исследовано получение активного гидроксида алюминия из щелочно-алюминатного раствора процесса Байера с помощью соли алюминия. Для этого была использована способность неравномерного роста кристаллов при низких температурах и без перемешивания. В результате образуется осадок с высокой удельной поверхностью, который легко растворяется в кислотах и щелочах. Экспериментально определена энергия активации получения активного гидроксида алюминия, которая составила 155,4 кДж/моль, что указывает на кинетический режим протекания процесса, несмотря на отсутствие перемешивания. Показана возможность применения полученного активного гидроксида алюминия в качестве затравки для производства хорошо откристаллизованного мелкодисперсного порошка гидроксида алюминия, который может быть использован для получения оксида алюминия неметаллургического назначения
ПОЛУЧЕНИЕ КАЧЕСТВЕННЫХ ЛИТЫХ ЗАГОТОВОК ИЗ Cu–Mg-СПЛАВОВ
Get PDFCu–Mg (0,1–1,0 %) alloy billet production process has been developed where continuous melting and continuous horizontal molding are realized in one melting-casting facility. In this case, the melt refining and homogenizing treatment is carried out continuously during the melting and casting time. The accepted technical solutions allow us to overcome the difficulties in magnesium precise content provision; eliminate high segregation in the melt; neutralize high surface activity of magnesium and its oxidation susceptibility; stabilize magnesium recovery from ligature and minimize the melt contamination with products of it oxidation; reach the deep metal refining from gases and nonmetallic inclusions; homogenize the melt in the chemical composition and provide obtaining high-quality billets.Разработана технология получения литых заготовок из Cu–Mg (0,1–1,0 %) сплавов, в которой процессы непрерывной плавки и непрерывного горизонтального литья реализованы в одном плавильно-литейном агрегате. При этом рафинирующая и гомогенизирующая обработка расплава осуществляется непрерывно в течение всего времени плавки и литья. Принятые для этого технические решения позволяют: преодолеть трудности обеспечения прецизионного содержания магния; устранить сильную ликвацию его в расплаве; нейтрализовать высокую поверхностную активность магния и склонность его к окислению; стабилизировать усвоение магния из лигатуры и минимизировать загрязнение расплава продуктами его окисления; достичь глубокого рафинирования металла от газов и неметаллических включений; гомогенизировать расплав по химическому составу и обеспечить получение высококачественных литых заготовок
ЛИНИЯ НЕПРЕРЫВНОГО НАНЕСЕНИЯ МЕТАЛЛИЧЕСКИХ ПОКРЫТИЙ НА ДЛИННОМЕРНЫЕ ИЗДЕЛИЯ ИЗ РАСПЛАВА
Get PDFThe paper describes the experience of designing and development of the line of continuous metallization of long-sized workpieces on the basis of a new principle of their horizontal movement through melt. A steel wire metallization plant has been developed for operation with zinc and aluminum melts. The investigations allow us to automatize its operation; equip it with modern devices for measurement of liquid metal level, temperature, wire speed, etc.; choose pneumatic devices for melt displacement from the furnace; develop the means to prepare the surface to metallization as well as the techniques for extra metal removal from wire.Представлен опыт создания и отработки линии непрерывной металлизации протяженных изделий на основе нового принципа их горизонтального перемещения в расплаве. Предложена установка металлизации стальной проволоки, которая работала с расплавами цинка и алюминия. Проведенные исследования позволили автоматизировать ее работу, оснастить современными приборами измерения уровня жидкого металла, температуры металла, скорости движения проволоки и т.д., подобрать средства пневмоавтоматики для вытеснения расплава из печи, разработать средства подготовки поверхности к металлизации, а также способы удаления лишнего металла с изделия
СКОРОСТЬ РАСТВОРЕНИЯ ОКСИДА СВИНЦА (II) В ЭКВИМОЛЬНОМ РАСПЛАВЕ KCl–PbCl2
Get PDFLead (II) oxide dissolution rates in equimolar KCl–PbCl2 melt at Т = 773, 823 & 873 K have been determined by gravimetrical method. In temperature rising from 773 to 873 K, the initial dissolution rate is shown to increase from 23,9 to 45,6 mg/(cm2·min) at the conditional factor of roughness equal to 10. Then the rate values for all temperatures are lined up and after 25 min they are close to zero, thus meaning the diffusion mode of the process at the natural convection conditions. The activation energy of PbO interaction with KCl–PbCl2 melt is 37,370±0,118 kJ/mol. The PbO limiting concentration in equimolar KCl–PbCl2 melt at temperatures 773, 823 and 873 K is 9,1; 10,6; 13,5 wt.% respectively. С помощью гравиметрического метода экспериментально определены скорости растворения (W) оксида свинца (II) в эквимолярном расплаве KCl–PbCl2 при Т = 773, 823 и 873 К. Показано, что с повышением температуры с 773 до 873 К на- чальная величина W возрастает с 23,9 до 45,6 мг/(см2·мин) при условном коэффициенте шероховатости, равном 10. Далее значения W для всех температур выравниваются и после 25 мин близки к нулю, что говорит о диффузионном режиме про- цесса в условиях естественной конвекции. Энергия активации процесса взаимодействия PbO c расплавом KCl–PbCl2 составила 37,370±0,118 кДж/моль. Определена предельная концентрация PbO в эквимолярном расплаве KCl–PbCl2, ко- торая при Т = 773, 823 и 873 К соответственно равна 9,1, 10,6 и 13,5 мас.%
КИНЕТИКА ОКИСЛЕНИЯ СПЛАВА АК7М2 + 0,05%Sr, ЛЕГИРОВАННОГО ГЕРМАНИЕМ
Get PDFThere was investigated by means of thermogravimetric method kinetics of oxidation of cutting alloy АК7М2 + 0,05%Sr, germanium alloyed, in air at temperature 773, 798 and 823 K. There was identified that additives until 0,05 wt.% Ge will be reduced oxidation rate, as evidenced by increasing of value of apparent activation energy of oxidation process from 14,7 to 79,8 kJ/mol, which with increasing of Ge content until 1,0 wt.% again decreased to 25,2 kJ/mol. The value of actual velocity of oxidation is changed in the range (4,30÷6,00)·10–4 kg/(m2·c) depending on quantity of alloying component. In products of alloys oxidation together with γ-Al2O3 looked up phases SiO2 and GeO2.Термогравиметрическим методом исследована кинетика окисления твердого сплава АК7М2 + 0,05%Sr, легированного германием, в атмосфере воздуха при температурах 773, 798 и 823 К. Выявлено, что добавки до 0,05 мас.% Ge уменьшают скорость окисления, о чем свидетельствует увеличение величины кажущейся энергии активации процесса окисления от 14,7 до 79,8 кДж/моль, которая с повышением содержания Ge до 1,0 мас.% снова падает до 25,2 кДж/моль. Величина истинной скорости окисления меняется в пределах (4,30÷6,00)·10–4 кг/(м2·с в зависимости от количества легирующего компонента. В продуктах окисления сплавов наряду с γ-Al2O3 также обнаружены фазы SiO2 и GeO2
ТЕРМОДИНАМИЧЕСКИЕ АСПЕКТЫ ВЫБОРА СЕРОСОДЕРЖАЩИХ СОБИРАТЕЛЕЙ ПРИ ФЛОТАЦИИ СУЛЬФИДНЫХ РУД
Get PDFInvestigations of complexing ability of sulfur-containing collectors in relation to ions of metals (Cu2 +, Ni2 +, Fe2 +, Co2 +) have been carried out at the temperature of 298 K and ionic strength of 0.075–0.75 mole/liter (NaNO3). It is established that potassium dibutyldithiophosphate possesses the largest affinity to metal ions among the phosphorus-containing collecting agents and Со2 + ion exhibits the maximum complexing ability. The rows of thermodynamic stability are obtained as well as the values of enthalpy, entropy, and Gibbs energy changes, temperature-dependent and temperature-independent contributions into ΔG0 of metal ion complexes with collector anions are calculated.Проведены исследования комплексообразующей способности серосодержащих собирателей по отношению к ионам металлов (Cu2+, Ni2+, Fe2+, Co2+) при температуре 298 К и ионной силе 0,075–0,75 моль/л (NaNo3). Установлено, что для фосфорсодержащих собирателей наибольшим сродством к ионам металлов обладает дибутилдитиофосфат калия, а максимальную комплексообразующую способность проявляет ион Со2+. Получены ряды термодинамической стабильности, а также рассчитаны величины изменения энтальпии, энтропии и энергии Гиббса, температурно-зависимые и температурно-независимые вклады в ΔG0 комплексов ионов металлов с анионами собирателей
ВЛИЯНИЕ pH СРЕДЫ НА АНОДНОЕ ПОВЕДЕНИЕ СПЛАВА Zn55Al, ЛЕГИРОВАННОГО СКАНДИЕМ
Get PDFThe anodic behavior of Zn55Al alloy doped with scandium has been studied. The scandium content dependence of the Zn55Al alloy corrosion potential shows the extreme character. The increase in the chloride ion concentration in the electrolyte reduces the corrosion potential. When doping element content grows in the alloys, pitting and repassivation potentials are shifted to the positive area, and when chloride ion concentration grows, the potentials are shifted to the negative area over the entire range of environment pH. Zn55Al alloy corrosion rate decreases 2–3 times in doping 0,005–0,05 wt.% scandium. Thus the alloys of such composition can be recommended as anode coating for corrosion protection of steel structures, components, and constructions.Исследовано анодное поведение сплава Zn55Al, легированного скандием. Установлен экстремальный характер зависимости потенциала коррозии этого материала от содержания в нем Sc и показано, что увеличение концентрации хлорид-ионов в электролите способствует уменьшению потенциала коррозии. Потенциалы питтингообразования и репассивации с ростом содержания легирующих элементов в сплавах смещаются в положительную, а с увеличением концентрации хлорид-ионов в отрицательную область во всем интервале рН среды. Скорость коррозии Zn55Al уменьшается в 2–3 раза при добавке в него 0,005–0,05 мас.% Sc, что позволяет рекомендовать сплав такого состава в качестве анодного покрытия для защиты от коррозии стальных конструкций, изделий и сооружений
О ВОЗМОЖНОСТИ ПРИМЕНЕНИЯ СЕРЫ ДЛЯ СУЛЬФИДИЗАЦИИ ТЕХНОГЕННЫХ ОТХОДОВ МЕДНОГО ПРОИЗВОДСТВА
Get PDFThere was investigated thermal characteristics and phase transformation of technological systems silt–sulfur, cake–sulfur and dust–sulfur. There was considered possibility of sulfur application for sulfidizing of copper production’s technogenic waste. There was defined that mechanism of sulfidizing of lead in technogenic waste by sulfur is common, and it refer to bond breaking lead–oxygen.Исследованы термические характеристики и фазовые превращения технологических систем шлам–сера, кек–сера и пыль–сера. Рассмотрена применимость серы для сульфидирования техногенных отходов медного производства. Установлено, что механизм сульфидирования серой соединений свинца в техногенных отходах является общим и относится к разрыву связи свинец–кислород
ЭКСПЕРИМЕНТАЛЬНЫЕ ИССЛЕДОВАНИЯ ЦЕМЕНТАЦИИ ОЛОВА В ДИСПЕРСНОЙ ФОРМЕ
Get PDFThe results of experimental investigations related to cementation extraction of tin in the dispersion form from sulfate solutions are described. The dependence of stationary aluminum potential on chlorine ion concentration in sulfate solution of divalent tin is shown. The polarization measurements of electrode processes of the Al–Sn galvanic cell have been carried out. The cementation conditions dependence of the dispersivity and bulk density of tin powder is establishedИзложены результаты экспериментальных исследований цементационного извлечения олова в дисперсной форме из сернокислых растворов. Показана зависимость стационарного потенциала алюминия от концентрации ионов хлора в сернокислом растворе двухвалентного олова. Проведены поляризационные измерения электродных процессов гальванопары Al–Sn. Установлена зависимость дисперсности и насыпной плотности оловянного порошка от условий проведения цементации
АЗОТНО-КИСЛОТНОЕ ВЫЩЕЛАЧИВАНИЕ ПОЛИМЕТАЛЛИЧЕСКИХ ПРОМПРОДУКТОВ ОБОГАЩЕНИЯ
Get PDFInvestigations concerning nitric acid leaching of polymetallic middlings for the purpose of maximum copper and zinc recoveryinto solution have been carried out. The optimal process parameters: L : S = 5, nitric acid consumption of 80 cm3 per 20 g weightedquantity, and process duration of 120 min were determined using the methods of mathematical design of the experiment.Проведены исследования по азотно-кислотному выщелачиванию полиметаллических промпродуктов с целью максимального извлечения меди и цинка в раствор. При помощи методов математического планирования эксперимента определены оптимальные параметры процесса: соотношение Ж : Т = 5, расход азотной кислоты – 80 см3 на 20 г навески,продолжительность процесса – 120 мин