No full textFranny Choi is a queer, Korean-American poet, playwright, teacher, organizer, pottymouth, GryffinClaw, and general overachiever. She is the author of Floating, Brilliant, Gone (2014), and a chapbook, Death by Sex Machine (2017). She has received awards from the Poetry Foundation and the Helen Zell Writers Program, as well as fellowships from the Vermont Studio Center and the Rhode Island State Council on the Arts. Her poems have appeared in journals including Poetry magazine, American Poetry Review, New England Review, and her work has been featured by the Huffington Post, PBS NewsHour, and Angry Asian Man
Prevention of hot cracking in Ni-based superalloy via passivation layer formation during additive manufacturing
No full textWe investigated the prevention of hot cracking in a non-weldable Ni-based superalloy by utilizing a passivation layer formed through laser-based directed energy deposition. The addition of Hf to the Ni-based superalloy facilitated the formation of a passivation layer consisting of Hf oxide on the surface of the as-deposited sample. An increase in the amount (thickness) of the passivation layers with increasing Hf content resulted in a reduction in hot cracking occurrence. Specifically, the addition of 2.5 wt% Hf led to the formation of uniformly distributed fine oxides without inducing hot cracks. This passivation layer effectively inhibited the formation of coarsened Mo oxides, which typically occur during oxidation in the liquid state and contribute to the hot cracking of Ni-based superalloy. During oxidation in the liquid state, Hf diffuses out to the surface and forms a passivation layer, thereby suppressing the formation and growth of oxides to sizes large enough to induce hot cracking
Oxidation behavior of AlN/CrN multilayered hard coatings
No full textAbstract We report on the oxidation behavior of AlN/CrN multilayers at 900 °C, deposited by radio frequency magnetron sputtering. It is shown that oxidation in this system is controlled by diffusion of Cr towards the surface and formation of Cr2O3. Cr diffusion is found to mainly occur along grain boundaries. Thus, coherent cubic AlN/CrN multilayer regions with coarse columnar grain structures are found to be oxidation resistant, whereas regions decomposed into hexagonal AlN/cubic CrN are prone to oxidation
A New Method for Mapping the 3D Atomic Distribution within Nanoparticles by Atom Probe Tomography (APT)
No full text
- …